Better living through pressure—functional nanomaterials made

2017-04-19 14:42 View:

Using pressure instead of chemicals, a Sandia National Laboratories team has fabricated nanoparticles into nanowire-array structures similar to those that underlie the surfaces of touch-screens for sensors, computers, phones and TVs. The pressure-based fabrication process takes nanoseconds. Chemistry-based industrial techniques take hours.


The process, called stress-induced fabrication, "is a new technology that mimics imprint processes already used by manufacturers," said Sandia researcher Hongyou Fan, who led the effort. "Only instead of embossing credit cards, we're using the same type of process to fabricate nanowires or other nano-sized components at ultrashort time scales."

The method, for which three patents have been issued, is 9 million times faster than any known chemical method when performed on Sandia's Veloce pulsed-power machine, which generates pressures on the order of 100,000 atmospheres, said Fan's colleague, Jack Wise.

Less exotically, for manufacturing instead of research, embossing machines similar to those already commercially in use could serve. "It's conceivable that few modifications would be needed to convert the machines from embossing to fabrication," Fan said.

The Sandia process saves:

  • time, because circuits can be fabricated in seconds instead of the hours required by chemical methods;

  • the environment, because there's no chemical waste to clean up;

  • materials, because exactly the amount needed is placed on a substrate.

Also, defects common in industrial chemical fabrication of semiconductors are reduced in number by the pressure process, which acts to fill any vacancies occurring in the product's atomic lattice.

"I have never seen or heard of this [process] in our extensive interaction with some of the leading material scientists in the world," said Tom Brennan of Chicago-based Arch Venture Partners, speaking in a video about an earlier version of the process. "It allows us to think of completely new material solutions to problems industry is facing across the board."

That earlier version of the pressure-based  worked by using a hand-tightened vise with diamond anvils, but that tool was not rapid or malleable enough for commercial production. Industrial embossing machines, on the other hand, produce sufficient pressure and are controllable.

"For a touch-screen, the pressure has to be worked out beforehand to stop the compression at just the right distance from the target: not too far, not too close, to produce the underlying nanowiring for a flat screen," said Fan. "It's a matter of programming the force applied to precisely determine how much to compress."

That is, for flat screens, the nanowires need to be made flexible enough to contact an electrically charged layer of the device when pressed by a finger, yet far enough apart to remain separate when there's no signal.

The technology, recently reported in Nature Communications, can fabricate a wide variety of nanoscale components including nanorods and nanosheets. The components can either be organized during their formation or dispersed in solvents for later assembly. The method could be used for  sensors, strain detectors and electrodes in solar cells.


Bio-magnetic beads, Sulfydryl modified
Huitong TM Samples mixed instrument|100%
Magnetic beads method glue recovery kit
Nano cerium oxide powder (CeO2 powder)
Nano Tungsten disulfide powder
Tungsten carbide nano powder (99.9% )
Nano Dy2O3 powder
Nano Cobalt powder (Nano Co powder)
Nano Aluminum oxide powder (Nano Al2O3Powder)
Nano Boron carbide powder (Nano CB4 Powder)
Tantalum carbide powder (nano particle size)
Nano titanium(Ti) Powder
Nano Titanium carbide powder (Nano TiC powder)
High purity Nano Manganese(Mn) powder
Nano SiO2 Powder
Nano Fe2O3 powder (99.9%)
Nano Aluminium Nitride powder (Nano AlN powder)
Nano Tungsten disulfide powder (Nano WS2 powder)
chitosan beads
aldehyde beads | aldehyde modified microsphere
Bio-magnetic beads, Carboxylic modified
Bio-magnetic beads, Amino modified
Bio-magnetic beads, Silicic modified
Magnetic fluid
Nano SiO2 dispersing agent
Nano Co dispersing agent
Nano oxidation zinc dispersing agent
Nano silver Soil antibacterial agent
Polyurethane release agents
Nano silver Powder (Nano Ag powder purity 99.99)
Thiadiazole-octyl mercaptan condensates(CAS No: 13539-13-4)
Dimercapto-thiadiazole dimerBis-DMTD
DMTD(2,5- dimercapto-1,3,4- thiadiazole)
Methylene bis (dibutyl dithio carbamate)
MoDTC Complexes (Solid MoDTC)
MoDTP (Liquid Molybdenum Dithiophosphate)
Nano Co dispersing agent
Water-based magnesium stearate
Polyurethane Internal Release Agent
Water-based zinc stearate (Vinyl lubricant )
Stearic acid amides emulsion for themal paper
Water-Based Calcium stearate
Coated with abrasive coating slurry